Brass sheets

The brass sheets are semi-finished products obtained by cold rolling, having good electrical and thermal conductivity, good cold deformation and embossing, good capacity for electroplating, soldering and welding and good resistance to corrosion.

COMMON AREAS OF USE FOR BRASS SHEETS:

furniture industry,
interior design,
cosmetic packaging,
components for the electrical industry,
armaments industry,
coin rounds,
medals and jewelry.

Download product sheet – PDF

ALLOYS FREQUENTLY USED IN BRASS PLATES AND STRIPS

Frequently used alloys

ALLOY	EN no.	Cu%	Zn%	Al%	Fe%	Ni%	Pb%	Sn%
CuZn37	CW508L	62,0-64,0	Rest	0,05	0,10	0,30	0,10	0,10
CuZn10	CW501L	89,0 – 91,0	Rest	0,02	0,05	0,30	0,05	0,10

Physical properties

ALLOY	EURONORM No	DENSITY	ELECTRICAL CONDUCTIVITY		THERMAL CONDUCTIVITY	MODULUS OF ELASTICITY
ALLOY	EURONORM No	g/cm3	MS/m	%IACS	W/mK	kN/m²
CuZn37	CW508L	8,44	16,0	28	116	110
CuZn10	CW501L	8,80	25,7	44	188	124

Mechanical properties

ALLOY	DELIVERY STATUS		MECHANICAL RESISTANCE, N/MM²		FLOW LIMIT, N/MM²	ELONGATION %		HARDNESS HV
ALLOY	DELIVERY STATUS		Min	Max	FLOW LIMIT, N/MM²	<2,5 mm	>2,5 mm	Min	Max
CuZn37	H055	R300	300	370	max. 180	38	48	55	90
	H095	R350	350	440	min. 170	19	28	95	125
	H125	R410	410	490	min. 300	8	12	120	155
	H150	R480	480	560	min. 430	3		150	180
	H170	R550	550		min. 500			170
CuZn10	H050	R240	240	290	max.140	36	45	50	80
	H080	R280	280	360	min.200	13	20	50	110
	H110	R350	350		min.290	4	8	110

Usual sizes

*Specific weight is a theoretical weight and may differ from the actual measured weight due to the geometric tolerance established in EN standards.

NAME	DIMENSION			WEIGHT KG/BUC.
NAME	b [mm]	d [mm]	L [mm]	WEIGHT KG/BUC.
Brass sheet	0.3	1000	2000	5.08
	0.4	1000	2000	6.78
	0.5	1000	2000	8.47
	0.6	1000	2000	10.16
	0.7	1000	2000	11.86
	0.8	1000	2000	13.55
	1.0	1000	2000	16.94
	1.5	1000	2000	25.41
	2.0	1000	2000	33.88
	2.5	1000	2000	42.35
	3.0	1000	2000	50.82
	4.0	1000	2000	67.76
	5.0	1000	2000	84.70
	6.0	1000	2000	101.64